High-T_c Josephson Junction Arrays Fabricated by He-FIB

verfasst von

Max Pröpper, Dominik Hanisch, Christoph Schmid, Marius Neumann, Paul Julius Ritter, Marc André Tucholke, Edward Goldobin, Dieter Koelle, Reinhold Kleiner, Meinhard Schilling, Benedikt Hampel

Abstract

The development of a fabrication process for Josephson junctions (JJs) using a direct-write helium-focused ion beam (He-FIB) technique provides the opportunity to control parameters such as the critical current <FOR VERIFICATION>$I$_c and normal-state resistance <FOR VERIFICATION>$R$_n of individual JJs in YBa₂Cu₃O_7-xJJ arrays. Such arrays could be used as a voltage calibration standard that is operated at higher temperatures and higher driving frequencies than the currently used niobium JJ arrays. This study presents the fabrication process of 79 YBa₂Cu₃O_7-xJJs in a meander array design using a direct writing He-FIB process with the same irradiation dose for all JJs. In this design, each of the JJs can be measured individually, and adjacent JJs that exhibit similar and suitable parameters for a voltage standard array can be measured in series. The scattering of the JJ parameters was investigated at 5 K and resulted in a spread in <FOR VERIFICATION>$I$_c of about 60% and in <FOR VERIFICATION>$R$_n of 25%. However, a couple of subarrays with a spread lower than 10% could be found. In addition, these JJ subarrays were irradiated with high-frequency radiation in the GHz and THz range at a temperature of 20 K and synchronization of up to three JJs was observed in both frequency ranges.

Externe Organisation(en)

Technische Universität Braunschweig
Eberhard Karls Universität Tübingen

Typ

Artikel

Journal

IEEE Transactions on Applied Superconductivity

ISSN

1051-8223

Publikationsdatum

12.12.2024

Publikationsstatus

Elektronisch veröffentlicht (E-Pub)

Peer-reviewed

Ja

ASJC Scopus Sachgebiete

Elektronische, optische und magnetische Materialien, Physik der kondensierten Materie, Elektrotechnik und Elektronik

Elektronische Version(en)

https://doi.org/10.1109/TASC.2024.3516741 (Zugang: Unbekannt)